Multi-composition gate dielectric field effect transistors

ABSTRACT

A first gate structure and a second gate structure are formed over a semiconductor material layer. The first gate structure includes a planar silicon-based gate dielectric, a planar high-k gate dielectric, a metallic nitride portion, and a first semiconductor material portion, and the second gate structure includes a silicon-based dielectric material portion and a second semiconductor material portion. After formation of gate spacers and a planarization dielectric layer, the second gate structure is replaced with a transient gate structure including a chemical oxide portion and a second high-k gate dielectric. A work-function metal layer and a conductive material portion can be formed in each gate electrode by replacement of semiconductor material portions. A gate electrode includes the planar silicon-based gate dielectric, the planar high-k gate dielectric, and a U-shaped high-k gate dielectric, and another gate electrode includes the chemical oxide portion and another U-shaped high-k gate dielectric.

BACKGROUND

The present disclosure relates to a method of forming a semiconductorstructure, and particularly to a method of forming multiple gatedielectrics having different compositions, and structures formed by thesame.

Gate dielectrics having different thicknesses are useful in providing avariety of field effect transistors on a same substrate. Replacementgate field effect transistors are compatible with high dielectricconstant (high-k) gate dielectrics and metal gates. However, integrationschemes that employ replacement gate field effect transistors tend tophysically expose silicon-oxide-based dielectric material portions todamaging etch processes prior to deposition of a high-k gate dielectricmaterial thereupon. In order to provide reliable semiconductor devicesof various types, an integration scheme is desired that allows use ofreplacement gate structures with multiple types of gate dielectricswithout damaging silicon-oxide-based dielectric material portions.

SUMMARY

A stack of a silicon-based dielectric material layer, a high dielectricconstant (high-k) material layer, and a metallic nitride layer is formedover a surface of a semiconductor substrate. The stack is patterned toremove the metallic nitride layer and the high-k material layer from oneregion, while another region is protected by a temporary mask layer. Asemiconductor material layer is subsequently deposited after removal ofthe temporary mask layer. The remaining portions of the stack of thesemiconductor material layer are patterned to form a first gatestructure including a planar silicon-based gate dielectric, a planarhigh-k gate dielectric, a metallic nitride portion, and a firstsemiconductor material portion, and a second gate structure including asilicon-based dielectric material portion and a second semiconductormaterial portion. After formation of gate spacers and a planarizationdielectric layer, the second gate structure is replaced with areplacement gate structure including a chemical oxide portion, a secondhigh-k gate dielectric, another metallic nitride portion, and a thirdsemiconductor material portion. Each of the first semiconductor materialportion and the third semiconductor material portion can be replacedwith a stack of a work-function metal layer and a conductive materialportion. A gate electrode includes the planar silicon-based gatedielectric, the planar high-k gate dielectric, and a U-shaped high-kgate dielectric, and another gate electrode includes the chemical oxideportion and another U-shaped high-k gate dielectric.

According to an aspect of the present disclosure, a method of forming asemiconductor structure is provided. A first material stack and a secondmaterial stack are formed on a semiconductor substrate. The firstmaterial stack includes at least a planar semiconductor oxide-baseddielectric portion and a first disposable material portion. The secondmaterial stack includes at least a second disposable material portion. Aplanarization dielectric layer is formed around the first and secondmaterial stacks. The second material stack is replaced with a stackincluding a chemical oxide layer and a U-shaped high-k dielectricportion. The first disposable material portion is removed. By depositionand planarization of a work function material layer and a conductivematerial layer, a first gate electrode is formed over the planarsemiconductor oxide-based dielectric portion, and a second gateelectrode is formed within a volume laterally bounded by the U-shapedhigh-k dielectric portion.

According to another aspect of the present disclosure, a semiconductorstructure includes a first field effect transistor and a second fieldeffect transistor located on a semiconductor substrate. The first fieldeffect transistor includes a first gate structure and the second fieldeffect transistor includes a second gate structure. The first gatestructure includes a stack of a planar semiconductor oxide-baseddielectric portion, a planar high dielectric constant (high-k)dielectric portion, and a first gate electrode. The second gatestructure includes a stack of a chemical oxide layer contacting asurface of the semiconductor substrate, a U-shaped high-k dielectricportion, and a second gate electrode laterally surrounded by verticalportions of the U-shaped high-k dielectric portion.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

FIG. 1 is a vertical cross-sectional view of a first exemplarysemiconductor structure after formation of a vertical stack including aplanar semiconductor oxide-based dielectric layer, a planar highdielectric constant (high-k) dielectric layer, and a planar metallicmaterial layer according to a first embodiment of the presentdisclosure.

FIG. 2 is a vertical cross-sectional view of the first exemplarysemiconductor structure after masking the vertical stack in a firstdevice region and removing physically exposed portions of the planarmetallic material layer and the planar high-k dielectric layer in asecond device region according to the first embodiment of the presentdisclosure.

FIG. 3 is a vertical cross-sectional view of the first exemplarysemiconductor structure after deposition of a disposable material layerand formation of a first material stack and a second material stack bypatterning the disposable material layer and remaining portions of thevertical stack according to the first embodiment of the presentdisclosure.

FIG. 4 is a vertical cross-sectional view of the first exemplarysemiconductor structure after formation of various source and drainregions, gate spacers, and a planarization dielectric layer according tothe first embodiment of the present disclosure.

FIG. 5 is a vertical cross-sectional view of the first exemplarysemiconductor structure after masking of the first material stack andremoval of a second disposable material portion according to the firstembodiment of the present disclosure.

FIG. 6 is a vertical cross-sectional view of the first exemplarysemiconductor structure after removal of a second planar semiconductoroxide-based dielectric portion according to the first embodiment of thepresent disclosure.

FIG. 7 is a vertical cross-sectional view of the first exemplarysemiconductor structure after formation of a chemical oxide layer, acontiguous high-k dielectric layer, a contiguous metallic materiallayer, and a fill material layer according to the first embodiment ofthe present disclosure.

FIG. 8 is a vertical cross-sectional view of the first exemplarysemiconductor structure after planarization of the fill material layer,the contiguous metallic material layer, and the contiguous high-kdielectric layer from above the top surface of the planarizationdielectric layer according to the first embodiment of the presentdisclosure.

FIG. 9 is a vertical cross-sectional view of the first exemplarysemiconductor structure after removal of a first disposable materialportion and a filler material portion according to the first embodimentof the present disclosure.

FIG. 10 is a vertical cross-sectional view of the first exemplarysemiconductor structure after deposition and planarization of acontiguous work function material layer and a conductive material layerand according to the first embodiment of the present disclosure.

FIG. 11 is a vertical cross-sectional view of a second exemplarysemiconductor structure after removal of a planar metallic materialportion and a U-shaped metallic material portion and deposition andplanarization of a contiguous work function material layer and aconductive material layer and according to a second embodiment of thepresent disclosure.

DETAILED DESCRIPTION

As stated above, the present disclosure relates to a method of formingmultiple gate dielectrics having different thicknesses, and structuresformed by the same. Aspects of the present disclosure are now describedin detail with accompanying figures. Like and corresponding elementsmentioned herein and illustrated in the drawings are referred to by likereference numerals. The drawings are not necessarily drawn to scale.Ordinals are used merely to distinguish among similar elements, anddifferent ordinals may be employed across the specification and theclaims of the instant application.

Referring to FIG. 1, a first exemplary semiconductor structure accordingto a first embodiment of the present disclosure includes a semiconductorsubstrate 8 that includes a semiconductor material layer 10. Varioussemiconductor devices including field effect transistors can besubsequently formed on the semiconductor material layer 10. Thesemiconductor substrate 8 can be a bulk substrate including a bulksemiconductor material constituting the semiconductor material layer 10throughout, or a semiconductor-on-insulator (SOI) substrate (not shown)containing a top semiconductor layer that constitutes a semiconductormaterial layer 10, a buried insulator layer (not shown) located underthe top semiconductor layer, and a bottom semiconductor layer (notshown) located under the buried insulator layer.

Various portions of the semiconductor material in the semiconductorsubstrate 8 can be doped with electrical dopants of p-type or n-type atdifferent dopant concentration levels. For example, the semiconductorsubstrate 8 may include at least one p-type well (not shown) and/or atleast one n-type well (not shown). Shallow trench isolation structures20 can be formed to laterally separate various surface regions of thesemiconductor substrate 8.

A planar semiconductor oxide-based dielectric layer 50L can be depositedon the top surface of the semiconductor substrate 8. As used herein, a“planar” element refers to an element having a uniform thicknessthroughout and does not include any vertically extending portion. Theplanar semiconductor oxide-based dielectric layer 50L includes asemiconductor-oxide based dielectric material. As used herein, a“semiconductor oxide-based dielectric material” refers to a dielectricmaterial that includes a semiconductor oxide as a predominant component.As used herein, a “predominant component” of a material refers to acomponent that accounts for more than 50% of all atoms within thematerial. As used herein, a “semiconductor material” can be any of theelemental semiconductor materials known in the art, an alloy of at leasttwo elemental semiconductor materials, a III-V compound semiconductormaterial, a II-VI compound semiconductor material, or a combinationthereof. As used herein, a “semiconductor oxide” refers to an oxide of asemiconductor material. A semiconductor oxide-based dielectric materialmay consist of a semiconductor oxide, a semiconductor oxynitride, or avertical stack of at least one semiconductor oxide layer and at leastone semiconductor oxynitride layer.

In one embodiment, the planar semiconductor oxide-based dielectric layer50L can be formed by thermal oxidation, a combination of thermaloxidation and thermal or plasma nitridation, plasma oxidation, acombination of plasma oxidation and thermal or plasma nitridation, of aphysically exposed top portion of the semiconductor material layer 10.The thickness of planar semiconductor oxide-based dielectric layer 50Lcan be in a range from 1.5 nm to 10 nm, although lesser and greaterthicknesses can also be employed. The planar semiconductor oxide-baseddielectric layer 50L can be formed as a single contiguous layer, or canbe formed in multiple portions that are laterally spaced from oneanother by the shallow trench isolation structures 20.

A planar high dielectric constant (high-k) dielectric layer 51L isformed on the top surface of the planar semiconductor oxide-baseddielectric layer 50L. The planar high-k dielectric layer 51L includes ahigh-k dielectric material. As used herein, a high-k dielectric materialrefers to a dielectric material having a dielectric constant greaterthan the dielectric constant of silicon nitride, i.e., 7.9. In oneembodiment, the high-k dielectric material of the planar high-kdielectric layer 51L can have a dielectric constant greater than 8.0. Inone embodiment, the high-k dielectric material layer can include adielectric metal oxide, which is a high-k material containing a metaland oxygen.

Dielectric metal oxides can be deposited by methods well known in theart including, for example, chemical vapor deposition (CVD), physicalvapor deposition (PVD), molecular beam deposition (MBD), pulsed laserdeposition (PLD), liquid source misted chemical deposition (LSMCD),atomic layer deposition (ALD), etc. Exemplary high-k dielectric materialinclude HfO₂, ZrO₂, La₂O₃, Al₂O₃, TiO₂, SrTiO₃, LaAlO₃, Y₂O₃,HfO_(x)N_(y), ZrO_(x)N_(y), La₂O_(x)N_(y), Al₂O_(x)N_(y), TiO_(x)N_(y),SrTiO_(x)N_(y), LaAlO_(x)N_(y), Y₂O_(x)N_(y), a silicate thereof, and analloy thereof. Each value of x is independently from 0.5 to 3 and eachvalue of y is independently from 0 to 2. The thickness of the planarhigh-k dielectric layer 51L can be from 0.9 nm to 6 nm, although lesserand greater thicknesses can also be employed. In one embodiment, theplanar high-k dielectric layer 51L may have an effective oxide thicknesson the order of or less than 2 nm. In an illustrative example, theplanar high-k dielectric layer 51L may be a hafnium oxide (HfO₂) layer.

A planar metallic material layer 53L can be formed on the top surface ofthe planar high-k dielectric layer 51L. The planar metallic materiallayer 53L includes a metallic material, which can be a conductivemetallic nitride, a conductive metallic carbide, an elemental metal, oran intermetallic alloy. In one embodiment, the planar metallic materiallayer 53L includes a conductive metallic nitride. In an illustrativeexample, the planar metallic material layer 53L can include titaniumnitride.

The material of the planar metallic material layer 53L can be deposited,for example, by physical vapor deposition (PVD), chemical vapordeposition (CVD), atomic layer deposition (ALD), vacuum evaporation, ora combination thereof. The thickness of the planar metallic materiallayer 53L can be in a range from 1 nm to 6 nm, although lesser andgreater thicknesses can also be employed.

The vertical stack of the planar semiconductor oxide-based dielectriclayer 50L, the planar high-k dielectric layer 51L, and the planarmetallic material layer 53L can be formed on the entirety of the topsurface of the substrate 8, which can include multiple device regions.The multiple device regions can include, for example, a first deviceregion R1 and a second device region R2.

Referring to FIG. 2, a masking layer 57 can be formed over the verticalstack of the planar semiconductor oxide-based dielectric layer 50L, theplanar high-k dielectric layer 51L, and the planar metallic materiallayer 53L. The masking layer 57 can be formed as a blanket (unpatterned)layer, and can be patterned to cover a top surface of the vertical stack(50L, 51L, 53L) in the first device region R1, while physically exposingthe vertical stack (50L, 51L, 53L) in the second device region R2. Inone embodiment, the masking layer 57 can be a photoresist layer that ispatterned employing lithographic methods.

The physically exposed portions of the planar metallic material layer53L and the planar high-k dielectric layer 51L in the second deviceregion R2 can be removed selective to the planar semiconductoroxide-based dielectric layer 50L by at least one etch, which can includean isotropic etch and/or an anisotropic etch. For example, a wet etchchemistry that etches the material of the planar metallic material layer53L can be employed in a first etch, followed by another wet etchchemistry that etches the material of the planar high-k dielectric layer51L selective to the material of the planar semiconductor oxide-baseddielectric layer 50L. The masking layer 57 can be subsequently removed,for example, by ashing.

Referring to FIG. 3, a disposable material layer is deposited directlyon the top surface of the planar metallic material layer 53L and on thetop surface of the planar semiconductor oxide-based dielectric layer50L. The disposable material layer includes a disposable material, i.e.,a material that is subsequently removed.

The disposable material layer includes a material that can besubsequently removed selective to the material of the planarsemiconductor oxide-based dielectric layer 50L and selective todielectric materials of gate spacers and a planarization dielectriclayer to be subsequently deposited above the top surface of thesemiconductor substrate 8. For example, the disposable material layercan include a semiconductor material such as silicon, germanium, asilicon germanium alloy, or a compound semiconductor material.Alternately, the disposable material layer can include any dielectricmaterial or any metallic material that can be removed selective to thedielectric materials of the gate spacer and the dielectric layer to besubsequently deposited. Yet alternately, the disposable material layercan include an organic material, amorphous carbon, or any otherdisposable fill material known in the art provided that the disposablefill material can be removed selective to the material of the planarsemiconductor oxide-based dielectric layer and selective to dielectricmaterials of gate spacers and a planarization dielectric layer to besubsequently deposited above the top surface of the semiconductorsubstrate 8. The thickness of the disposable material layer can be in arange from 30 nm to 600 nm, although lesser and greater thicknesses canalso be employed. In an illustrative example, the disposable materiallayer can include polysilicon.

The stack of the disposable material layer, the planar metallic materiallayer 53L, the planar high-k dielectric layer 51L, and the planarsemiconductor oxide-based dielectric layer 50L is subsequentlylithographically patterned to form material stacks. For example, aphotoresist layer (not shown) can be applied over the disposablematerial layer, and can be lithographically patterned to cover areas inwhich formation of material stacks is desired. The pattern in thephotoresist layer can be transferred through the stack of the disposablematerial layer, the planar metallic material layer 53L, the planarhigh-k dielectric layer 51L, and the planar semiconductor oxide-baseddielectric layer 50L by at least etch, which can include at least oneanisotropic etch. Remaining portions of the stack of the disposablematerial layer, the planar metallic material layer 53L, the planarhigh-k dielectric layer 51L, and the planar semiconductor oxide-baseddielectric layer 50L constitute various material stacks. The last stepof the etch that removes physically exposed portions of the planarsemiconductor oxide-based dielectric layer 50L can be selective to thesemiconductor material of the semiconductor material layer 10. Thephotoresist layer can be subsequently removed, for example, by ashing.

A first material stack (50A, 51, 53, 55A) can be formed in the firstdevice region R1, and a second material stack (50B, 55B0 can be formedin the second device region R2. The sidewalls of various elements withinthe same material stack can be vertically coincident with one another.As used herein, two surfaces are vertically coincident with each otherif the two surfaces are located within the same vertical plane.

The first material stack (50A, 51, 53, 55A) can include a first planarsemiconductor oxide-based dielectric portion 50A, a planar high-kdielectric portion 51, a planar metallic material portion 53, and afirst disposable material portion 55A. The second material stack (50B,55B) can include a second planar semiconductor oxide-based dielectricportion 50B and a second disposable material portion 55B. The first andsecond planar semiconductor oxide-based dielectric portions (50A, 50B)are remaining portions of the planar semiconductor oxide-baseddielectric layer 50L, the planar high-k dielectric portion 51 is aremaining portion of the planar high-k dielectric layer 51L, the planarmetallic material portion 53 is a remaining portion of the planarmetallic material layer 53L, and the first and second disposablematerial portions (55A, 55B) are remaining portions of the disposablematerial layer.

The planar high-k dielectric material portion 51 can contact the firstplanar semiconductor oxide-based dielectric portion 50A, and underliesthe first disposable material portion 55A. The planar metallic materialportion 53 can contact the planar high-k dielectric material portion 51and the first disposable material portion 55A. The second disposablematerial portion 55B can contact the second planar semiconductoroxide-based dielectric portion 50B.

Referring to FIG. 4, gate spacers 52 can be formed on sidewalls of eachof the material stacks, for example, by deposition of a conformaldielectric material layer and an anisotropic etch. The conformaldielectric material layer includes a dielectric material that isresistant to the etch chemistry to be subsequently employed to removethe disposable material portions (55A, 55B). For example, the conformaldielectric material layer can include silicon oxide, silicon nitride,silicon oxynitride, a high dielectric constant dielectric materialhaving a dielectric constant greater than 7.9 and including a dielectricoxide of a metal, or combinations thereof. The conformal dielectricmaterial layer can be deposited, for example, by chemical vapordeposition (CVD) or atomic layer deposition (ALD). The anisotropic etchremoves horizontal portions of the conformal dielectric material layer.Remaining vertical portions of the conformal dielectric material layerconstitute the gate spacers 52.

At least one masked ion implantation process and/or at least one unmaskion implantation process can be performed before and/or after formationof the gate spacers 52. If a masked ion implantation is employed, amasking structure including a combination of a patterned maskingmaterial layer (not shown) and the material stacks (50A, 51, 53, 55A,50B, 55B) can be employed during the masked ion implantation process. Ifan unmasked ion implantation process is employed, the material stacks(50A, 51, 53, 55A, 50B, 55B) can be employed as a masking structureduring the unmasked ion implantation process. The at least one ionimplantation process can form various doped active regions (16A, 16B)within the semiconductor material layer 10. As used herein, doped activeregions collectively refer to source regions, drain regions, sourceextension regions, and drain extension regions as known in the art. Eachdoped active region (16A, 16B) can have a doping of an oppositeconductivity type than the portion of the semiconductor material layer10 in which the doped active region (16A, 16B) is formed.

A planarization dielectric layer 70 can be formed above the doped activeregions (16A, 16B) and at least up to the height of the top surface ofthe material stacks (50A, 51, 53, 55A, 50B, 55B). The planarizationdielectric layer 70 includes a dielectric material such as siliconoxide, silicon nitride, silicon oxynitride, a dielectric metal oxide,porous or non-porous organosilicate glass, or a combination thereof. Inone embodiment, the planarization dielectric layer 70 includes adielectric material that is resistant to the etch chemistry to besubsequently employed to remove the disposable material portions (55A,55B).

In one embodiment, the planarization dielectric layer 70 includes aspin-on dielectric material. In one embodiment, the planarizationdielectric layer 70 can be formed by chemical vapor deposition (CVD)and/or atomic layer deposition (ALD). The planarization dielectric layer70 can be planarized employing the top surfaces of the disposablematerial portions (55A, 55B) as stopping surfaces. The planarization ofthe planarization dielectric layer 70 can be effected, for example, by arecess etch or chemical mechanical planarization (CMP). If CMP isemployed, the top surfaces of the gate spacers 52 can be employed asstopping surfaces for the planarization step. The top surface of theplanarization dielectric layer 70 can be coplanar with the top surfacesof the disposable material portions (55A, 55B). Thus, the planarizationdielectric layer 70 is formed over the semiconductor substrate 8 andaround the material stacks (50A, 51, 53, 55A, 50B, 55B).

Referring to FIG. 5, a mask layer 77 is formed over the planarizationdielectric layer 70, and is patterned to cover the first device regionR1, while not covering the second device region R2. The mask layer 77can be, for example, a photoresist layer. The patterning of the masklayer 77 can be performed employing any method known in the art. Forexample, if the mask layer 77 is a photoresist layer, the mask layer 77can be patterned employing lithographic exposure and development. Thefirst material stack (50A, 51, 53, 55A) is masked by the patterned masklayer 77, and the second disposable material portion 55B is subsequentlyremoved.

The second disposable material portion 55B in the second device regionR2 is removed selective to the gate spacers 52 and the planarizationdielectric layer 70 while the patterned mask layer 77 prevents removalof the first disposable material portion 55A that is present in thefirst device region R1. For example, if the second disposable materialportion 55B includes a polycrystalline semiconductor material, theremoval of the second disposable material portion 55B can be performedby an isotropic or anisotropic dry etch employing hydrochlorocarbons,hydrogen chloride, and/or any other etchant that removes a semiconductormaterial selective to dielectric materials such as silicon oxide orsilicon nitride. The removal of the second disposable material portion55B may, or may not, be selective to the dielectric material of thesecond planar semiconductor oxide-based dielectric portion 50B. A gatecavity, which is herein referred to as a gate cavity 59B, is formed inthe volume from which the second disposable material portion 55B isremoved.

Referring to FIG. 6, the second planar semiconductor oxide-baseddielectric portion 50B is removed by an etch, which can be an isotropicetch or an anisotropic etch. In one embodiment, the second planarsemiconductor oxide-based dielectric portion 50B can be removedselective to the gate spacers 52 employing a wet etch chemistry. In anillustrative example, if the gate spacer 52 includes silicon nitride,the second planar semiconductor oxide-based dielectric portion 50B canbe removed by a wet etch employing hydrofluoric acid. Collateral etchingof the planarization dielectric layer 70 may occur depending on thecomposition of the planarization dielectric layer 70 and the etchchemistry. The patterned mask layer 77 can be subsequently removed, forexample, by ashing.

Referring to FIG. 7, a chemical oxide layer 80 may be formed bytreatment of exposed semiconductor surfaces underneath the gate cavity59B with a chemical. For example, the process step for this wet chemicaloxidation may include treating a cleaned semiconductor surface (such asa semiconductor surface treated with hydrofluoric acid) with a mixtureof ammonium hydroxide, hydrogen peroxide and water (in a 1:1:5 ratio) ata temperature about 65° C. Alternately, the chemical oxide layer 80 canalso be formed by treating the HF-last semiconductor surface in ozonatedaqueous solutions, with the ozone concentration usually varying from,but not limited to, 2 parts per million (p.p.m.) to 40 p.p.m. Thechemical oxide layer 80 helps minimize mobility degradation in thesemiconductor material layer 10 due to a high-k dielectric material tobe subsequently formed on the chemical oxide layer 80. In case thesemiconductor material layer 10 is a silicon layer, the chemical oxidelayer 80 is a silicon oxide layer. Typically, the thickness of thechemical oxide layer 80 is from 0.1 nm to 0.4 nm, although lesser andgreater thicknesses can also be employed.

A contiguous high-k dielectric layer 81L is formed directly on the topsurface of the chemical oxide layer 80 and the sidewall surface of agate spacer 52 in the second device region R2 and the top surfaces ofthe planarization dielectric layer 70. The contiguous high-k dielectriclayer 81L can be a single contiguous layer of a dielectric materialhaving a dielectric constant greater than 7.9. The contiguous high-kdielectric layer 81L can be a conformal layer having a same thickness atvertical portions and at horizontal portions. The contiguous high-kdielectric layer 81L can be formed on the chemical oxide layer 80, thetop surface of the planarization dielectric layer 70, and the topsurface of the first disposable material portion 55A.

The contiguous high-k dielectric layer 81L can be formed employing anyof the methods that can be employed to form the planar high-k dielectriclayer 51L. Further, the contiguous high-k dielectric layer 81L caninclude any of the high-k dielectric material that can be employed forthe planar high-k dielectric layer 51L. The thickness of the contiguoushigh-k dielectric layer 81L can be from 0.9 nm to 6 nm, although lesserand greater thicknesses can also be employed. The thickness of thecontiguous high-k dielectric layer 81L may be greater than, equal to, orless than, the thickness of the planar high-k dielectric layer 51L. Thecomposition of the contiguous high-k dielectric layer 81L can be thesame as, or different from, the composition of the planar high-kdielectric layer 51L.

A contiguous metallic material layer 82L can be formed on the surfacesof the contiguous high-k dielectric layer 81L. The contiguous metallicmaterial layer 82L can be a contiguous conductive material layer. Thecontiguous metallic material layer 82L can be a conformal layer or anon-conformal layer. The contiguous metallic material layer 82L can beformed employing any of the methods that can be employed to form theplanar metallic material layer 53L. Further, the contiguous metallicmaterial layer 82L can include any of the metallic material that can beemployed for the planar metallic material layer 53L. The thickness ofthe contiguous metallic material layer 82L can be in a range from 1 nmto 6 nm, although lesser and greater thicknesses can also be employed.The thickness of the contiguous metallic material layer 82L may begreater than, equal to, or less than, the thickness of the planarmetallic material layer 53L. The composition of the contiguous metallicmaterial layer 82L can be the same as, or different from, thecomposition of the planar metallic material layer 53L.

A fill material layer 84L is deposited on the contiguous metallicmaterial layer 82L, for example, by chemical vapor deposition (CVD),physical vapor deposition (CVD), or vacuum evaporation. The fillmaterial layer 84L includes a material that can be subsequently removedselective to the metallic material of the contiguous metallic materiallayer 82L. For example, the fill material layer 84L can include asemiconductor material such as silicon, germanium, a silicon germaniumalloy, or a compound semiconductor material. Alternately, the fillmaterial layer 84L can include any dielectric material or any metallicmaterial that can be removed selective to the metallic material of thecontiguous metallic material layer 82L. Yet alternately, the fillmaterial layer can include an organic material, amorphous carbon, or anyother disposable fill material known in the art provided that thedisposable fill material can be removed selective to the material of themetallic material of the contiguous metallic material layer 82L.

The material of the fill material layer 84L may, or may not, be the sameas the material of the first disposable material portion 55A (which isderived from the disposable material layer). The thickness of the fillmaterial layer 84L is selected such that the gate cavity 59B (See FIG.6) is completely filled by the fill material layer 84L. In oneembodiment, the thickness of the fill material layer 84L, as measuredabove the top surface of the planarization dielectric layer 70, can bein a range from 30 nm to 600 nm, although lesser and greater thicknessescan also be employed. In an illustrative example, the fill materiallayer 84L can include polysilicon.

Thus, a stack of material layers fill the gate cavity 59B. The stack ofmaterial layers include the chemical oxide layer 80, the contiguoushigh-k dielectric layer 81L, the contiguous metallic material layer 82L,and the fill material layer 84L.

Referring to FIG. 8, the portions of the fill material layer 84L, thecontiguous metallic material layer 82L, and the contiguous high-kdielectric layer 81L located above the top surface of the planarizationdielectric layer 70 can be removed by a planarization process. Theplanarization process can include a recess etch, chemical mechanicalplanarization (CMP), or a combination thereof. The remaining portion ofthe contiguous high-k dielectric layer 81L after the planarizationprocess is herein referred to as a U-shaped high-k dielectric portion81. The remaining portion of the contiguous metallic material layer 82Lafter the planarization process is herein referred to as a U-shapedmetallic material portion 82. The remaining portion of the fill materiallayer 84L after the planarization process is herein referred to as afill material portion 84.

As used herein, a “U-shaped” element refers to an element that includesa pair of vertical portions and a horizontal portion such that thebottommost sub-portions of the vertical portions are adjoined to thehorizontal portion. The processing steps of FIGS. 5-8 replaces thesecond stack structure (50B, 55B) with a stack including the chemicaloxide layer 80, the U-shaped high-k dielectric portion 81, the U-shapedmetallic material portion 82, and the fill material portion 84.

Referring to FIG. 9, the first disposable material portion 55A and thefiller material portion 84 can be removed selective to the planarizationdielectric layer 70 and the gate spacers 52. In one embodiment, theremoval of the first disposable material portion 55A and the fillermaterial portion 84 can be selective to the material of the planarmetallic material portion 53 and the U-shaped metallic material portion82. The removal of the first disposable material portion 55A and thefiller material portion 84 can be performed by an etch, which can be anisotropic etch or an anisotropic etch. In one embodiment, if the firstdisposable material portion 55A and the filler material portion 84include semiconductor materials, a dry etch or a wet etch employinghydrofluorocarbon etchant and/or hydrogen chloride can be employed toetch the first disposable material portion 55A and the filler materialportion 84. The removal of the first disposable material portion 55A andthe filler material portion 84 may be performed simultaneously, or oneof the first disposable material portion 55A and the filler materialportion 84 may be removed prior to, or after, removal of the other ofthe first disposable material portion 55A and the filler materialportion 84. In one embodiment, the fill material portion 84 can beremoved simultaneously with removal of the first disposable materialportion 55A. A first gate cavity 85A is formed in a volume from whichthe first disposable material portion 55A, and a second gate cavity 85Bis formed in a volume from which the fill material portion 84 isremoved.

The combination of the first planar semiconductor oxide-based dielectricportion 50A and the planar high dielectric constant (high-k) dielectricportion 51 constitutes a first gate dielectric (50A, 51), which is thegate dielectric of a first field effect transistor to be formed in thefirst device region R1. The entirety of the first gate dielectric (50A,51) is planar, and has a uniform thickness throughout.

The combination of the chemical oxide layer 80 and the U-shaped high-kdielectric portion 81 constitutes a second gate dielectric (80, 81),which is the gate dielectric of a second field effect transistor to beformed in the second device region R2. The second gate dielectric (80,81) is a U-shaped gate dielectric having vertical portions and ahorizontal portion. Each vertical portion of the second gate dielectric(80, 81) is a vertical portion of the U-shaped high-k dielectric portion81, and the horizontal portion of the second gate dielectric (80, 81) isa stack of the horizontal portion of the U-shaped high-k dielectricportion 81 and the chemical oxide layer 80. In one embodiment, eachvertical portion of the second gate dielectric (80, 81) can have auniform lateral thickness, and each horizontal portion of the secondgate dielectric (80, 81) can have a uniform vertical thickness.

Referring to FIG. 10, a contiguous work function material layer and aconductive material layer can be deposited in the first and second gatecavities (85A, 85B) and over the planarization dielectric layer 70. Thecontiguous work function material layer can include any conductivematerial that can affect the work function of the first and second fieldeffect transistors to be formed in the first and second device regions(R1, R2). Exemplary materials that can be employed for the contiguouswork function material layer include, but are not limited to, TiN, TaN,WN, Ti, Ta, and W. The contiguous work function material layer can bedeposited, for example, by chemical vapor deposition (CVD), physicalvapor deposition (PVD), atomic layer deposition (ALD), or a combinationthereof. The thickness of the contiguous work function material layercan be in a range from 1 nm to 30 nm, although lesser and greaterthicknesses can also be employed. In one embodiment, multiple contiguouswork function material layers may be employed in lieu of a singlecontiguous work function material layer.

The conductive material layer includes a conductive material, which canbe an elemental metal, an intermetallic alloy, a conductive metallicnitride, a conductive metallic oxide, a doped semiconductor material, ora combination thereof. The thickness of the deposited conductivematerial layer is selected such that the first and second cavities (85A,85B) are completely filled with the conductive material layer. Theconductive material layer can be deposited, for example, by chemicalvapor deposition (CVD), physical vapor deposition (PVD), atomic layerdeposition (ALD), or a combination thereof.

Excess portions of the conductive material layer and the contiguous workfunction material layer can be removed from above the top surface of theplanarization dielectric layer 70 by a planarization process, which canemploy, for example, chemical mechanical planarization (CMP). Remainingportions of the contiguous work function material layer in the first andsecond device regions (R1, R2) constitute a first U-shaped work functionmaterial portion 86A and a second U-shaped work function materialportion 86B, respectively. Remaining portions of the conductive materiallayer in the first and second device regions (R1, R2) constitute a firstconductive material portion 88A and a second conductive material portion88B, respectively.

The assembly of the planar metallic material portion 51, the firstU-shaped work function material portion 86A, and the first conductivematerial portion 88A constitutes a first gate electrode (53, 86A, 88A),which functions as the gate electrode of the first field effecttransistor in the first device region R1. The assembly of the U-shapedmetallic material portions 82, the second U-shaped work functionmaterial portion 86B, and the second conductive material portion 88Bconstitutes a second gate electrode (82, 86B, 88B), which functions asthe gate electrode of the second field effect transistor in the seconddevice region R2.

The first gate electrode (53, 86A, 88A) is formed over the first planarsemiconductor oxide-based dielectric portion 50A, and the second gateelectrode (82, 86B, 88B) is formed within a volume laterally bounded bythe U-shaped high-k dielectric portion 81 by deposition andplanarization of the contiguous work function material layer and theconductive material layer. The first gate electrode (53, 86A, 88A)includes the first U-shaped work function material portion 86A and thefirst conductive material portion 88A. The second gate electrode (82,86B, 88B) includes the second U-shaped work function material portion86B and the second conductive material portion 88B. The first and secondU-shaped work function material portions (86A, 86B) can have the samecomposition and the same thickness.

The first field effect transistor includes a first gate structure, whichincludes a stack of the first gate dielectric (50A, 51) and the firstgate electrode (53, 86A, 88A). The second field effect transistorincludes a second gate structure, which includes a stack of the secondgate dielectric (80, 81) and the second gate electrode (82, 86B, 88B).The second gate electrode (82, 86B, 88B) is laterally surrounded byvertical portions of the U-shaped high-k dielectric portion 81.

In one embodiment, the semiconductor material layer 10 of thesemiconductor substrate 8 can include a semiconductor material, and thefirst planar semiconductor oxide-based dielectric portion 50A caninclude a dielectric material selected from a dielectric oxide of thesemiconductor material and a dielectric oxynitride of the semiconductormaterial. In one embodiment, the first planar semiconductor oxide-baseddielectric portion 50A can have a greater thickness than the chemicaloxide layer 80.

In one embodiment, the planar high-k dielectric portion 51 can have adifferent composition or a different thickness than the U-shaped high-kdielectric portion 81. In one embodiment, the first U-shaped workfunction material portion 86A contacts a top surface of the planarmetallic material portion 53, and the second U-shaped work functionmaterial portion 86B contacts the U-shaped metallic material portion 82.The U-shaped metallic material portion 82 can be in contact with theU-shaped high-k dielectric portion 81 and the second U-shaped workfunction material portion 86B. The planar metallic material portion 53and the U-shaped metallic material portion 82 can have differentcompositions or have different thicknesses.

Referring to FIG. 11, a second exemplary semiconductor structureaccording to a second embodiment of the present disclosure can bederived from the first exemplary semiconductor structure of FIG. 9 byremoving the planar metallic material portion 53 from underneath thefirst gate cavity 85A and the U-shaped metallic material portion 82 fromaround the second gate cavity 85B, and by subsequently performing theprocessing steps of FIG. 10. The removal of the planar metallic materialportion 53 and the U-shaped metallic material portion 82 can beperformed selective to the gate spacers 52 and the materials of theplanar high-k dielectric portion 51 and the U-shaped high-k dielectricportion 81. For example, the removal of the planar metallic materialportion 53 and the U-shaped metallic material portion 82 can beperformed employing a wet etch chemistry that etches metallic materialsselective to dielectric materials.

Due to the absence of a planar metallic material portion or a U-shapedmetallic material portion at the processing steps corresponding to theprocessing steps of FIG. 10, the first U-shaped work function materialportion 86A is formed directly on the top surface of the planar high-kdielectric portion 51, and the second U-shaped work function materialportion 86B is formed directly on the top surface and inner surfaces ofthe U-shaped high-k dielectric portion 81.

The assembly of the first U-shaped work function material portion 86Aand the first conductive material portion 88A constitutes a first gateelectrode (86A, 88A), which functions as the gate electrode of the firstfield effect transistor in the first device region R1. The assembly ofthe second U-shaped work function material portion 86B and the secondconductive material portion 88B constitutes a second gate electrode(86B, 88B), which functions as the gate electrode of the second fieldeffect transistor in the second device region R2.

The first gate electrode (86A, 88A) is formed over the first planarsemiconductor oxide-based dielectric portion 50A, and the second gateelectrode (86B, 88B) is formed within a volume laterally bounded by theU-shaped high-k dielectric portion 81 by deposition and planarization ofthe contiguous work function material layer and the conductive materiallayer. The first gate electrode (86A, 88A) includes the first U-shapedwork function material portion 86A and the first conductive materialportion 88A. The second gate electrode (86B, 88B) includes the secondU-shaped work function material portion 86B and the second conductivematerial portion 88B. The first and second U-shaped work functionmaterial portions (86A, 86B) can have the same composition and the samethickness.

The first field effect transistor includes a first gate structure, whichincludes a stack of the first gate dielectric (50A, 51) and the firstgate electrode (86A, 88A). The second field effect transistor includes asecond gate structure, which includes a stack of the second gatedielectric (80, 81) and the second gate electrode (86B, 88B). The secondgate electrode (86B, 88B) is laterally surrounded by vertical portionsof the U-shaped high-k dielectric portion 81.

In one embodiment, the semiconductor material layer 10 of thesemiconductor substrate 8 can include a semiconductor material, and thefirst planar semiconductor oxide-based dielectric portion 50A caninclude a dielectric material selected from a dielectric oxide of thesemiconductor material and a dielectric oxynitride of the semiconductormaterial. In one embodiment, the first planar semiconductor oxide-baseddielectric portion 50A can have a greater thickness than the chemicaloxide layer 80.

In one embodiment, the planar high-k dielectric portion 51 can have adifferent composition or a different thickness than the U-shaped high-kdielectric portion 81. In one embodiment, the first U-shaped workfunction material portion 86A contacts a top surface of the planarhigh-k dielectric portion 51, and the second U-shaped work functionmaterial portion 86B contacts the U-shaped high-k dielectric portion 81.Thus, the planar metallic material portion 53 can be in contact with thetop surface of the planar high-k dielectric portion 51 and the bottomsurface of the first U-shaped work function material portion 86A.

The various embodiments of the present disclosure can be employed toprovide multiple types of gate dielectrics having different thicknesses.Particularly, the first gate dielectric (50A, 51) can be a planar gatedielectric having a uniform thickness throughout, and the second gatedielectric (80, 81) can be U-shaped gate dielectric having verticalportions and horizontal portions. The planar high-k dielectric portion51 protects the first planar semiconductor oxide-based dielectricportion 50A throughout the processing steps of the present disclosure.The integrity and reliability of the first planar semiconductoroxide-based dielectric portion 50A, and thus, the integrity of the firstgate dielectric (50A, 51), can be enhanced over prior art schemes inwhich a top surface of a planar semiconductor oxide-based dielectricportion is subjected to an etchant during an etch process or a precleanprocess.

While the disclosure has been described in terms of specificembodiments, it is evident in view of the foregoing description thatnumerous alternatives, modifications and variations will be apparent tothose skilled in the art. Each of the various embodiments of the presentdisclosure can be implemented alone, or in combination with any otherembodiments of the present disclosure unless expressly disclosedotherwise or otherwise impossible as would be known to one of ordinaryskill in the art. Accordingly, the disclosure is intended to encompassall such alternatives, modifications and variations which fall withinthe scope and spirit of the disclosure and the following claims.

What is claimed is:
 1. A method of forming a semiconductor structurecomprising: forming a first material stack and a second material stackon a semiconductor substrate, said first material stack including atleast a planar semiconductor oxide-based dielectric portion and a firstdisposable material portion, and said second material stack including atleast a second disposable material portion; forming a planarizationdielectric layer around said first and second material stacks; replacingsaid second material stack with a stack including a chemical oxide layerand a U-shaped high-k dielectric portion; removing said first disposablematerial portion; and forming a first gate electrode over said planarsemiconductor oxide-based dielectric portion and a second gate electrodewithin a volume laterally bounded by said U-shaped high-k dielectricportion by deposition and planarization of a work function materiallayer and a conductive material layer.
 2. The method of claim 1, whereinsaid first material stack comprises a planar high dielectric constant(high-k) dielectric material portion contacting said planarsemiconductor oxide-based dielectric portion and underlying said firstdisposable material portion.
 3. The method of claim 2, wherein saidfirst material stack further comprises a planar metallic materialportion contacting said planar high-k dielectric material portion andsaid first disposable material portion.
 4. The method of claim 1,wherein said second material stack further includes another planaroxide-based dielectric portion that contacts a bottom surface of saidsecond disposable material portion.
 5. The method of claim 1, furthercomprising masking said first material stack with a patterned mask layerformed over said first material stack and said planarization dielectriclayer while removing said second material stack.
 6. The method of claim1, further comprising: forming a contiguous high-k dielectric layer onsaid chemical oxide layer, a top surface of said planarizationdielectric layer, and a top surface of said first disposable materialportion; and removing portions of said contiguous high-k dielectriclayer from above a top surface of said planarization dielectric layer,wherein a remaining portion of said contiguous high-k dielectric layeris said U-shaped high-k dielectric portion.
 7. The method of claim 1,further comprising: forming a stack of a contiguous metallic materiallayer and a fill material layer in a cavity formed by removal of saidsecond material stack; and removing portions of said contiguous metallicmaterial layer and said fill material layer from above said top surfaceof said planarization dielectric layer.
 8. The method of claim 7,further comprising removing a remaining portion of said fill materiallayer simultaneously with removal of said first disposable materialportion.
 9. The method of claim 1, wherein said first gate electrodecomprises a first U-shaped work function material portion and a firstconductive material portion, and said second gate electrode comprises asecond U-shaped work function material portion and a second conductivematerial portion, wherein said first and second U-shaped work functionmaterial portions have a same composition and a same thickness.
 10. Themethod of claim 9, wherein said first material stack further comprises aplanar metallic material portion contacting said planar high-kdielectric material portion, and said method further comprises forming aU-shaped metallic material portion on said U-shaped high-k dielectricportion, wherein said first U-shape work function material portion isformed on said planar metallic material portion, and said secondU-shaped work function material portion is formed on said U-shapedmetallic material portion.
 11. A semiconductor structure comprising afirst field effect transistor and a second field effect transistorlocated on a semiconductor substrate, said first field effect transistorcomprising a first gate structure and said second field effecttransistor comprising a second gate structure, wherein said first gatestructure comprises a stack of a planar semiconductor oxide-baseddielectric portion, a planar high dielectric constant (high-k)dielectric portion, and a first gate electrode, and wherein said secondgate structure comprises a stack of a chemical oxide layer contacting asurface of said semiconductor substrate, a U-shaped high-k dielectricportion, and a second gate electrode laterally surrounded by verticalportions of said U-shaped high-k dielectric portion.
 12. Thesemiconductor structure of claim 11, wherein said planar high-kdielectric portion has a different composition or a different thicknessthan said U-shaped high-k dielectric portion.
 13. The semiconductorstructure of claim 11, wherein said semiconductor substrate comprises asemiconductor material, and said planar semiconductor oxide-baseddielectric portion comprises a dielectric material selected from adielectric oxide of said semiconductor material and a dielectricoxynitride of said semiconductor material.
 14. The semiconductorstructure of claim 11, wherein said planar semiconductor oxide-baseddielectric portion has a greater thickness than said chemical oxidelayer.
 15. The semiconductor structure of claim 11, wherein said firstgate electrode comprises a first U-shaped work function material portionand a first conductive material portion, and said second gate electrodecomprises a second U-shaped work function material portion and a secondconductive material portion.
 16. The semiconductor structure of claim15, wherein said first and second U-shaped work function materialportions have a same composition and a same thickness.
 17. Thesemiconductor structure of claim 15, wherein said first U-shaped workfunction material portion contacts a top surface of said planar high-kdielectric portion, and said second U-shaped work function materialportion contacts said U-shaped high-k dielectric portion.
 18. Thesemiconductor structure of claim 15, wherein said first gate electrodefurther comprises a planar metallic material portion in contact with atop surface of said planar high-k dielectric portion and a bottomsurface of said first U-shaped work function material portion.
 19. Thesemiconductor structure of claim 18, wherein said second gate electrodefurther comprises a U-shaped metallic material portion in contact withsaid U-shaped high-k dielectric portion and said second U-shaped workfunction material portion.
 20. The semiconductor structure of claim 19,wherein said planar metallic material portion and said U-shaped metallicmaterial portion have different compositions or have differentthicknesses.